Composition | After grinding epoxy resin, pigment and filler, additive and organic solvent are added to form A component, polyurethane ester curing agent is component B. | ||||
Application | It is used for protection of cement floor and decorative painting and covering. | ||||
Basic parameters | Wet film thickness 70-85um | Dry film thickness 30-40 um | 0.13-0.25 kg/㎠ theoretical dosage | ||
Drying time:Surface dry 2H / Overall dry 24H | |||||
Water resistance:Nothing unusual about 48 hours of immersion | |||||
Washing resistance greater than 10000 times | |||||
Gasoline resistant (SH0004-1990(1998) solvent oil ,1 hour) no abnormal | |||||
Bending test less than or equal to 2 mm | |||||
Recommended number of painting routes | 2 | ||||
Repainting interval | Not less than 24h | ||||
Base temperature | above 3 ℃ Celsius above dew point | ||||
Coating method | air spraying, airless spraying, brush coating | ||||
Mix ratio | Main paint : Curing agent: Diluent =3:1:0.5(weight ratio) |