Coating type | HL-001 penetrating epoxy primer | ||
Flash point | 7° | Solid volume ratio | About 40% |
Dilution ratio | (Volume ratio) not more than 10% | colour | Transparent |
proportion | About 0.97 (g/cm³) | luster | bright |
Dry film thickness | 40um | The mixing ratio | Main agent/curing agent (weight ratio) |
Wet mold thickness | 100um | Package weight | 20kg |
Theoretical coating amount | About 10Square meter/kg |
Coating type | HL-001-1 Solvent-free epoxy base coat paint | ||
Flash point | 7° | Solid volume ratio | About 40% |
Dilution ratio | (Volume ratio) not more than 10% | colour | Transparent |
proportion | About 1.5(g/cm³) | luster | bright |
Dry film thickness | 90um | The mixing ratio | Main agent/curing agent (weight ratio)Summer type 2:1 |
Wet mold thickness | 100um | Package weight | 20kg |
Theoretical coating amount | About 3kg/Square meter |
Coating type | HL-002 epoxy intermediate coating high solids coating | ||
Color and appearance of paint film | Various colors, flat and smooth | Alkali resistance (10%HCL) | About 40% |
Adhesion (1mm grid) level | ≤1 | Pencil hardness | ≥HB |
Viscosity (25°) | 1000±500CPS | Acid resistance (10%HCL) | Transparent |
Impact resistance | ≥50 | Abrasion resistance (500g, 1000 revolutions) | bright |
Surface dry | ≤4h | Ratio | Main agent/curing agent (weight ratio) |
Hard work | ≤24h |
Coating type | HL-003 solvent epoxy resin surface finish coating | ||
Dilution rate | DR-100 | colour | See special color card |
Dilution ratio | (Volume ratio) not more than 10% | luster | bright |
proportion | About 1.7 (g/cm³) white | The mixing ratio | Main agent/curing agent (weight ratio) 4:1 |
Dry film thickness | 40um | Package weight | 20kg |
Theoretical coating amount | Approximately 11.3Square meter/kg, the dry film thickness of coating is 40um, and the amount of coating varies depending on the substrate, the constructor and the construction method. | Wet film thickness | 88um |
Solid volume ratio | About 45% |
Coating type | HL-003-1 epoxy resin high gloss finish coating | ||
proportion | About 1.5 (g/cm³) | colour | See special color card |
Dry film thickness | 80um | Construction method | Roll coating, spraying |
Solid volume ratio | About 99±1 | luster | highlight |
Theoretical coating amount | Approximately 11.3Square meter/kg, the dry film thickness of coating is 40um, and the amount of coating varies depending on the substrate, the constructor and the construction method. | The mixing ratio | Main agent/curing agent (volume ratio) 4:1 |
Pencil hardness | 3h | Package weight | 20kg |
Skfekeeping
1.Sealed and stored in a cool and dry indoor place , at a temperature of 5~35°,storage period is 18 months.
2.Do not mix with other solvents,paints,powders,etc.
3.After the coating is opened,it should be avoided to store for a long time ,and it must be completely sealed after use.
EpOXY RESIN PAINT
epoxy resin paint is a kind of thermoplastic epoxy oilgomer and it is a
substance that is in liquid,viscous or soild state and other forms.
Time interval rolling scraping painting:
Make sure that each time the material is dry and then apply the next material.
After 8hours of normal cortuction , the next layer can be constructed .The mortar layer is theick , and the drying time is prolonged when the temperature is low
CONSTRUCTION CONDITIONS
1.SUBSTRATE REQUIRMENTS
The costing surface of architectural coatings must be dry , fiem, clean and smooth;
DRY:floor humidity is lower than 6% RH,PH value is lower than 10
Firmness: no powedered loose material , no loose patent leather on the old ground
clean:No oil ,grease ,mildew,algae and other adherents.
2.PRECAUTIONS FOR CONSTRUCTION
This product can be appropriately added with dilument depending on different construction methods
and construction environments,but the dilution ratio should be strictly controlled. Excessive dilution is
strictly prohibited. The main agent and the curing agent must be mixed in the correct ratio . The main
agent is first stirred with an electric mixer ,and then slowly added to the curing Agent ,stir well evenly.