Alumina al2o3 Ceramic Beads Strung
Alumina Ceramic Beads is manufactured by dry press method and sintered at temperature upto 1650 C. All the material is prepared by Gongtao. The production is under careful material selection of high grade alumina spray drying granulation from what we call calcined alumina, thus the quality stability is maximally ensured. It enjoys high temperature resistance, excellent insulating property, and efficient thermal conductivity and heat transfer. Thanks to its property, the ceramic beads is widely used as components of flexible ceramic heating pad and channel heaters at operation of pre and postweld heat treatment; Welding process, stress-relieving, ship-building, other heat-resistance-environment. Compared with hot press method
Advantages: Higher density, higer surface finish and unifomity than heat press cast method, excellent thermal condictivity and heat transfer, resistance against thermal shock and mechanical abuse.
Application: As ceramic parts of flexible pad and channel heaters at operations of pre and postweld heat treatment; Welding process, stress-relieving, pre-heating & post heating, ship-building, other resistance-heating environment.
Alumina Content: | 95% |
Bulk Density Fired: | 3.7g/cm3 |
Grain Size: | 6um |
Rockwell Hardness: | 78(R45N) |
Mohs Hardness: | 9 |
Flexural Strength: | 320 Mpa |
Compressive Strength: | 2000 MPa |
Thermal Conductivity: | 21W/ m3 |
Young's Modulus: | 325 Gpa |