Project | Test Standard | The Test Conditions | Unit | DG-417 |
Tensile Strength | ISO 527 | 50mm/min,4.0mm | Mpa | 48 |
Elongation at Break | ISO 527 | 50mm/min,4.0mm | % | 35 |
Flexural Strength | ISO 178 | 4mm,2.0mm/min | Mpa | 72 |
Flexural Modulus | ISO 178 | 4mm,2.0mm/min | Mpa | 2265 |
Izod impact strength | ISO 180 | 23℃,4.0mm | KJ/m2 | 19 |
Rockwell hardness | GB/T9342 | R-Scale | 108 | |
HeatDeflection temperature | ISO 75 | 1.8MPa,laid flat 9.8-15mm | ℃ | 75 |
Vicat Softening Point | ISO 306 | 50N,50℃/hr,3-6.5mm | ℃ | 100 |
Flammability | UL94 | 1.5mm | HB | |
Melt Flow Rate | ISO 1133 | 220℃ 10KG | g/10min | 19 |
Specific Gravity | ISO 1183A | 23℃ | 1.04 | |
features | Universal injection grade |