General Description: * The wear plate is manufactured by depositing high chromium, wear resistant materials on the mild steel base plate using open arc or submerged arc welding process. * Consistent wear resistance guaranteed from surface down to 75% depth of the overlay. * The volume fraction of primary carbides is maintained between 30 to 50% to provide a good combination of wear resistance and homogenous bonding. * Plate hardness ranges from HRC58-65. The hardness is tested on machined flat surface just below overlay surface. * Fine cracks perpendicular to the welding bead is normal due to natural stress relieving in a very hard matrix. * Staggered cracking pattern on overlay surface contributes to good formability. * The wear plate is suitable for severe wear and moderate impact applications. | | |
Typical Applications: Acme plate is widely used in the mining, power plant, port, cement, steel plant, glass, waste handling, glass, dredging, pulp and paper industries. Some applications are as below: * Mining: Hopper and bin liners, Chute and feeder liners, dump truck body liners, dozer blades, shovel buckets, dragline buckets, excavators. * Cement: Separator guide blades, vertical mixer liners, conveying pipelines, screw conveyors, distributors, sintering ore conveying chute, hopper liners * Power: Pipelines, coal feeder chutes, coal hoppers,coal mill shell liner, classifier cones, journal liners, deflectors. * Steel: Bin liners, hopper liners, coke vibrating screen plates, housing liners, sintering fan blade, discharging ducts. | | |
Product name | Acme Wear Plates | |
| hardfacing by open arc welding or submerged arc welding | |
| Q235/Q345B+Chromium carbide overlay alloy
| |
Certificate | ISO9001:2008 | |
| | |
| | |
| Chromium carbide hard particles volume fraction above 50 % The maximum hardness of chromium carbide is HV 1800 | |
| ASTM G65 methode A: 0.08~0.18 g according to different alloy, and the wear resistance of CCO plate is 30 times higher than low carbon stell and 12 times than heat treated steel
| |
| withstand medium impact and moderate impact
| |
| withstand temperatures up to 600 ℃, customized high temperature resistance wear plates according to customer's requirements which can withstand maximum terperatures up to 900 ℃
| |
| | |
| Uniform overlay thickness, with tolerance within 0~0.5 mm
| |
Surface treatment | hardfacing, cladding, open arc or submerged arc welding | |
| Open arc welding: 1.4x3.4; 1.5x3.0; 2.0x3.0 meter, customized Submerged arc welding: 1400*3000 mm, 1400*3500 mm, 2100*3500 mm, customized | |
| backing plate (mild steel )thickness (mm) | wear resistant alloy layer thickness (mm) |
| | |
3 on 3, 4 on 4, 5 on 5 4 on 6, 5 on 6, 6 on 6, 8 on 6 4 on 8, 5 on 8, 6 on 8, 7 on 8, 8 on 8 4 on 10, 5 on 10, 6 on 10, 7 on 10, 8 on 10, 9 on 10, 10 on 10, 20 on 10 4 on 12, 5 on 12, 6 on 12, 7 on 12, 8 on 12, 10 on 12, 11 on 12, 12 on 12 6 on 14, 8 on 14, 10 on 14 6 on 16, 8 on 16, 10 on 16 6 on 18, 8 on 18, 10 on 18 5 on 20, 6 on 20, 8 on 20, 10 on 20, 20 on 20, 10 on 30, 10 on 40 Customized | | |
Product Advantages | 1, ACME company Cr content in overlay is 25-40%.other company cr content is 10-20%. 2, ACME company the carbide( cr7c3) volume fraction on the micros tructure is above 50%. other company below 30%. 3, ACME company hardness HRC58-65. other company hardness below HRC58. 4, ACME company uniform overlay. other company non-uniform overlay. 5, ACME company smooth surface. other company uneven. 6, ACME company high wear resistance. other company poor wear resistance. | |
Thickness(backing plate + overlay) | W x L (mm) | |
4+4, 5+5 | 1,400 x 3,000 | |
6+6, 8+5, 8+6, 8+7, 8+8, etc | 1,400 x 3,500 | |
10+8, 10+9, 10+10, 10+20, 12+12, 12+20, 12+32, 12+50,14+26, 14+32, 20+30, customized thickness | 1,400 x 3,500 2,100 x 3,500 | |
C | 3.5-6.0 | |
Si | 1.0-3.0 | |
Mn | 1.0-3.0 | |
Cr | 27-40 | |
Others | Mo Nb V W Ni B etc | |
Fe | Balance | |
Note: Alloy content varies in different plate thickness. Chemical composition, hardness, alloy content, thickness, size could be customized. | | |
The backing mild steel plate provides ACME overlay plates with structural integrity, which makes our overlay plates fabricated without damage to welding overlay, regardless of the shape and complexity of the structure.ACME has the capabilities to manufacture and further process such fabrications or to supply formed, read-to-go wear liners. | | |
Cutting: ACMEoverlay plates could be cut by plasma, water-jet, laser. Plasma cutting is the recommended method for cutting our plate. | | |
Drilling: Straight holes and countersunk holes. | | |
Studs Welding: ACME plate can be fabricated with studs welded to backing of wear plate (M12, M16, M20 and M24), manually or automatically. | | |
Joint Welding: ACME wear plate can be welded and assembled into kinds of wear parts. | | |
Our factory: ACME COMPANYis located in Tianjin city, China's northern international shipping center. We are specialized in researching, developing and producing wear resistant products with many years experience in this field. We have more than 300 employees, with an annual capacity 140,000 m² wear plates and 9,000 tons of welding consumables. | | |