BUCKET WEAR BUTTONS FOR MINING WEAR PARTS AND CONSTRUCTION WEAR PARTS WB90
Hyster wear system is more than just a product. It is a combination of products, services and metallurgical expertise to provide superior wear protection for mining equipment and other industrial applications. A key part of this package is the Bimetallic Wear Products, a comprehensive offering of buttons, blocks, bars, runners, tiles and overlay plate to match any application.
Hyster White Iron Wear Block(700BHN-63HRC)-- Range of products based on a composite white iron wear surface metallurgically bonded to a weldable mild steel backing plate. Wear block is fixed to the surface of fixed and mobile plant equipment, such as mining buckets and chutes, where protection from severe abrasion is required.
Hyster Overlay Wear Plates--Chromium carbide clad wear plate manufactured in HYSTER and marketed worldwide. Overlay plate is well suited to fixed and mobile plant equipment associated with the construction, mining and resource industries; particularly iron ore, coal, cement and steel applications.
Hyster NiHard--Abrasion and high impact resistant product. It is often cast into billets and liners and used extensively in the mining, construction and mineral processes industries, particularly in bulk handling situations.
Hyster Tungsten Carbide—High standard abrasion resistant product. It is often used where the application has no impact force or very slightly impact.
Features and Benefits
Reduced Maintenance
• Protects any high wear area, eliminating the need for frequent rebuild or replacing wear plate
• Lasts longer than other wear protection
• Excellent alternative to hard facing which can lead to cracking of major structural components Increased Productivity
• Reduced maintenance ensures maximum machine availability
• Wide variety of shapes and sizes allows small areas to be protected, minimizing the affect on penetration and material flow
Lower Operating Cost
• Can be fit to flat or curved surfaces, eliminating the need to have wear plate formed to fit
• Bucket life is significantly increased, minimizing repair and new bucket orders
Typical Data Numbers:
>white iron wear blocks life is 50% greater than that of Ni Hard Irons.
>At least 7 times longer than A.R. type steels 360/400 BHN
>5 times the wear rate of Manganese Steel
>3 times the wear rate of Tapco Weld Hardfacing
>4 times the wear rate of Astralloy-Vulcan
>16 times the wear rate of Carbon Steel
>3 times the wear rate of 500 BHN A.R. Plate
The unique, formable design of Hyster-Wear chocky bars are available in various lengths, grades and sizes and can also be customized as per the clients specific need. Applications for Chocky Bars are wide and varied, ranging from specific wear protection on buckets for loaders, excavators and draglines machines, or for weld-on hammer tips for the re-cycling industry, or chute linings and rock box edges.
They are easy to use and install. They can be bent, cut and formed to suit different surfaces.
The standard is 23mm thick, length is 240mm, width could be from 25mm from 150mm. We can also produce according to your special requests .
Type: Notched type and Non-notched type
ITEM NO. | DIMENSION(mm) | N.W.(kg) |
CB 25 | 240x25x23 | 0.9 |
CB 40 | 240x40x23 | 1.5 |
CB 50 | 240x50x23 | 1.9 |
CB 65 | 240x65x23 | 2.5 |
CB 80 | 240x80x23 | 3.2 |
CB 90 | 240x90x23 | 3.5 |
CB 100 | 240x100x23 | 3.9 |
CB 130 | 240x130x23 | 5.4 |
CB 150 | 240x130x23 | 6.0 |
**Other dimension is also available against your inquiry.**
Hardness:63HRC/700BHN
Chrome carbide+mild steel
High wear resistance+good impact toughness
OEM SERVICE, OEM MANUFACUTRER, OEM LOGO FREE!
Perfect solution for ground engaging applications as on adaptor teeth, shovels, buckets, heavy earth moving equipment etc, to provide wear protection or security under the toughest impact and wear abrasion circumstance.
C |
Cr |
Mn |
Mo |
Cu |
P |
Si |
S |
B.V.Nb |
2.5-3.5 |
15-18 |
0.5-1.0 |
0.5-2.5 |
0.5-1.0 |
0.02max |
0.5-1.0 |
0.02max |
0.1-0.5 |
B. Mechanical Property:
1) Tensile Strength 630Mpa Min.
2) Shearing Strength 250Mpa Min.
3) Hardness 63 HRC
C. Micro-structure
High grade quality with competitive prices, we also pleased to offer you free samples and OEM service.