ü RUTH MS-902 HIGH MOUDLUS HIGH ELASTICITY Adhesive Sealant for home decoration
ü MS Polymer based Sealant. The functionalized polyether backbone with methoxysilane terminal groups provides excellent performances and makes MS Polymer-based products unique and beneficial.
ü The workmanship and raw material is from Japan
ü Applicable to the surrounding of doors and windows indoor decoration and structure sealing.
ü MS-902 Mainly used for sealing cracks with little requirement of displacement ability but high demand for puncture resistance and pressure resistance
Ø High Modulus, high flexible, it suits for sealing bond strength required seal
Ø Mono- component, good output, does not slump in vertical joints;
Ø Environment friendly (no solvent, free isocyanate ), totally chemical neutral and odorless;
Ø Strong initial strength, suitable for fast positioning;
Ø No yellowing, high level of anti-mold;
Ø Good sealing and waterproof property.
Test Index | MS-902 |
Basis | hybrid MS polymer |
Appearance | Black/white /gray /transparent |
Density (g/cm3) | 1.3±0.1 |
Rigidity (Shore A) | 40 ~50 |
Skin formation time (min) | ≤180 |
Hardening time (mm/24h) | ≥2 |
Output (g/min) | ≥ 100 |
Elongation at break % | ≥300 |
Tensile strength Mpa | ≥5.00 |
Module E,Mpa 23℃ | >0.4 |
Module E,Mpa -20℃ | >0.6 |
Fixed adhesion | No destruction |
Adhesion after immersion | No destruction |
Adhesion after cold drawn or Hot Press | No destruction |
Elastic recovery percentage,% | ≥60 |
Temperature Range | -40℃~90℃ |
Shelf Life | 12 months |
Store in a cool, dry place at 5-30°C, avoid exposing to sun and rain
600ml / piece. 20pieces / carton 19kgs/Carton
The Prints on the sealant can change to your stickers
Shelf life 12 months