It adheres strongly to the products of nonferrous metals like zinc, aluminum and aluminum alloy, as well as stainless steel, etc.
It is a preferred anticorrosive primer for nonferrous metals.
Mixing ratio: Main agent/Firming agent=8/1(by weight)
Standard film thickness: Dry: 30μm/coat
Theoretical spreading rate: 0.09kg/ m2/30μm
Solid contents: 71.3%
Humidity requirement: below 85%
Drying time & Coating interval
Temperature°C
Dry to touch min
Dry semi-hard hrs
Min. interval hrs
Max. interval d | -10 0 10 20 30
4 2.5 2 1.5 1
36 24 14 10 8
36 24 14 10 8
|