Products name | Aluminum plate |
Thickness(mm) | aluminum sheet:0.15-6.0 aluminum plate:6.0-25.0 |
Width(mm) | 20-2000 |
Standard | GB, JIS, DIN, ASTM |
Surface treatment | Brushed, Mirror, Embossed, Sandblasted, etc |
Temper | O/H111 H112 H116/H321 H12/H22/H32 H14/H24/H34/H16/H26/H36 H18/H28/H38 H114/H194, etc. |
Type | coil/sheet/strips/plate |
Package | Standard export package,such as wooden box or as required. |
1000 Series | Industrial Pure Aluminum(1050,1060 ,1070, 1100) |
2000 Series | Aluminum-copper alloys(2024(2A12), LY12, LY11, 2A11, 2A14(LD10), 2017, 2A17) |
3000 Series | Aluminum-manganese alloys(3A21, 3003, 3103, 3004, 3005, 3105) |
4000 Series | Al-Si alloys(4A03, 4A11, 4A13, 4A17, 4004, 4032, 4043, 4043A, 4047, 4047A) |
5000 Series | Al-Mg alloys(5052, 5083, 5754, 5005, 5086,5182) |
6000 Series | Aluminum Magnesium Silicon Alloys(6063, 6061, 6060, 6351, 6070, 6181, 6082, 6A02) |
7000 Series | Aluminum, Zinc, Magnesium and Copper Alloys(7075, 7A04, 7A09, 7A52, 7A05) |
Mechanical Property | ||||||||||||||||
ALUMINUM ALLOY | Grade | Normal Temper | Temper | Tensile Strength N/mm² | Yield Strength N/mm² | Elongation% | Brinell Hardness HB | |||||||||
Plate | Bar | |||||||||||||||
1XXX | 1050 | O,H112,H | O | 78 | 34 | 40 | - | 20 | ||||||||
1060 | O,H112,H | O | 70 | 30 | 43 | - | 19 | |||||||||
Al-Cu (2XXX) | 2019 | O,T3,T4,T6,T8 | T851 | 450 | 350 | 10 | - | - | ||||||||
2024 | O,T4 | T4 | 470 | 325 | 20 | 17 | 120 | |||||||||
Al-Mn (3XXX) | 3003 | O,H112,H | O | 110 | 40 | 30 | 37 | 28 | ||||||||
3004 | O,H112,H | O | 180 | 70 | 20 | 22 | 45 | |||||||||
Al-Si (4XXX) | 4032 | O,T6,T62 | T6 | 380 | 315 | - | 9 | 120 | ||||||||
Al-Mg (5XXX) | 5052 | O,H112,H | H34 | 260 | 215 | 10 | 12 | 68 | ||||||||
5083 | O,H112,H | O | 290 | 145 | - | 20 | - | |||||||||
Al-Mg-Si (6XXX) | 6061 | O,T4,T6,T8 | T6 | 310 | 275 | 12 | 15 | 95 | ||||||||
6063 | O,T1,T5,T6,T8 | T5 | 185 | 145 | 12 | - | 60 | |||||||||
Al-Zn-Mg (7XXX) | 7003 | T5 | T5 | 315 | 255 | 15 | - | 85 | ||||||||
7075 | O,T6 | T6 | 570 | 505 | 11 | 9 | 150 |