High saturate magnetic flux density ----- Minimize transformer volume
High permeability --------------------------- Promote efficiency of transformers
low coercivity --------------------------------- Reduce distributional capacitance
Low core loss -------------------------------- Minimize temperature rise of transformers
Excellent stability --------------------------- The highest serving temperature of 130 ℃ for long time
Saturate Magnetic Flux Density (T) | 1.25 | Saturate Magnetostriction | 2*10-6 |
Curie Temerature (℃) | 560 | Density (g/cm3) | 7.2 |
Crystallization Temperature (℃) | 510 | Resistivity (cm) | 130 |
hardness Hv (kg/mm2) | 880 |
Transverse Field Annealed | No Field Annealed | Longitudinal Feild Annealed | |
Initial Permeability | >3*104 | >8*104 | >1*104 |
Maximum Permeability | >5*104 | >45*104 | >50*104 |
Remanence (T) | <0.2 | <0.6 | <0.85 |
Coercivity (A/m) | <1.8 | <0.8 | <1.8 |
Core Loss (W/kg) (20kHz, 0.5T) |
<50 | <25 | <90 |
Core Loss (W/kg) (100kHz, 0.3T) |
<150 | 150 | <300 |
Variation of Core Loss (-55-125) | <15% | <15% | <15% |
Type | No. | Width (mm) | Thickness ( μm) |
First Generation Cast Ribbon | 1K107 | 5-50 | 28-34 |
Second Generation Cast Ribbon | 1K107B | 55 | 26±2 |
60 | |||
65 | |||
50 | |||
Second Generation Slitting Ribbon | 1K107B | 6.5 | |
8 | |||
10 | |||
15 | |||
20 | |||
25 | |||
30 | |||
35 | |||
40 | |||
45 | |||
Second Generation Slitting Ribbon | 1K107B | 40 | |
45 | |||
50 | |||
Third Generation Cast Ribbon | 1K107B | 55 | 22±2 |
60 | |||
65 | |||
65 | |||
Third Generation Slitting Ribbon | 1K107B | 8 | |
10 | |||
15 | |||
20 | |||
25 | |||
30 | |||
35 | |||
40 | |||
45 | |||
50 | |||
Fouth Generation Cast Ribbon | 55 | 18±2 | |
60 | |||
65 | |||
70 | |||
Fouth Generation Slitting Ribbon | 8 | ||
10 | |||
15 | |||
20 | |||
25 | |||
30 | |||
35 | |||
40 | |||
45 | |||
50 |
Transformer cores for high frequenc swithc mode power supplies
Current transformer cores for electric industry
Transformer cores for ground-fault-interrupters
EMC common mode chokes
Sensor Cores
Cores for saturable reactors, magnetic amplifiers, beads, pluse compressors etc.
Location: Lujiang Economic Development Zone, Hefei, China
Registered Capital: RMB 11 million
Establishment time: 1993
Facilities Volume: More than 5000 square meter
Your feedback is very important to us. We would love to hear from you.
Contact us:
Judy Liu
lizhi2(at)magneticmateiral.net.cn
Skype:Judyliu0619