1500C Castables
Low Cement Refractory Castables is product that is used in various part of furnace as Monolithic Refractories that added hydraulic alumina cement to refractory aggregate.Our company is producing suitable product to installation and working condition through a quality control,this product which is minimizing alumina cement for using various dispersants and ultra fine powder so it has excellent abrasion resistance,erosion resistance,spalling resistance and chemical resistance.It widely used in part of various industrial furnace including incinerator,nonferrous metal furnace etc.
Specification for Low Cement Refractory Castables is as following:
No. | A-45 | A-60 | A-70 | A-75 | A-80 | A-90 | |
Dry Density (g/cm3) ≥ | 2.3 | 2.5 | 2.6 | 2.65 | 2.7 | 3 | |
Chemical (%) | Al2O3≥ | 45 | 60 | 70 | 75 | 80 | 90 |
ZrO2 | -- | -- | -- | -- | -- | -- | |
Modulus of Rupture(Mpa) | 110oC×24h≥ | 5 | 8 | 9 | 9 | 10 | 12 |
1500oC×3h≥ | 8(1350oC) | 10 (1450oC×3h) | 12 | 15 | |||
Compressive Strength(Mpa) | 110oC×24h≥ | 30 | 40 | 40 | 45 | 45 | 60 |
1450oC×3h≥ | 60 | 80 | 80 | 85 | 90 | 85 | |
Linear Dimensional Change After Fired (1500oC×3h)%≤ | ±0.5 | ±0.5 | ±0.5 | ±0.5 | ±0.5 | ±0.5 | |
1350oC×3h | 1450oC×3h | 1450oC×3h | 1450oC×3h | ||||
Refractoriness(oC)≥ | 1710 | 1740 | 1790 | 1790 | 1790 | 1790 | |
Working Temp(oC) | 1450 | 1450 | 1500 | 1550 | 1600 | 1650 |
Application of Low Cement Refractory Castables :
Material for metallurgy, petroleum, chemical and other industries kilns
Part of refining installation, like ladle cover
Insert for roof of the kiln