Alloy | process | Thickness (mm) | ||
Thickness(mm) | Width(mm) | Length(mm) | ||
C1100 | Hot rolling | 4-8 | 600-2000 | ≤5000 |
>8-60 | 200-3000 | ≤6000 | ||
>60-150 | 200-3000 | ≤6000 | ||
Cold rolling | 0.3-0.5 | ≤600 | ≤2000 | |
>0.5-3.0 | ≤1020 | ≤3000 | ||
>3.0-1.2 | ≤3000 | ≤6000 |
Mechanical Properties
Alloy | Temper | Thickness(mm) | Rm/OViran2) Tensile Strength | A11.3/% Elongtion | Hardness(Hv) |
C1100 | R | 4-14 | Rm≥195Mpa | A11.3≥30% | - |
. 14 | - | - | - | ||
M | >0.5 | Rm≥205Mpa | A11.3≥30% | ≤70 | |
Y4 | Rm=215~275Mpa | A11.3≥25% | 60-90 | ||
Y2 | Rm=245~345Mpa | A11.3≥8% | 80-110 | ||
Y | Rm≥295~380Mpa | - | 90-120 | ||
T | Rm≥350Mpa | - | ≥110 |